Ultrafast Growth of Single-crystal Graphene Assisted by a Continuous Oxygen Supply
 
XZ Xu, ZH Zhang, L Qiu, JN Zhuang, L Zhang, H Wang, CN Liao, HD Song, RX Qiao, P Gao, ZH Hu, L Liao, ZM Liao, DP Yu, EG Wang, F Ding*, HL Peng*, KH Liu*, Nature Nanotech. 2016, 11, 930-935. 
 

ABSTRACT: Graphene has a range of unique physical properties1,2 and could be of use in the development of a variety of electronic, photonic and photovoltaic devices3–5. For most applications, large-area high-quality graphene films are required and chemical vapour deposition (CVD) synthesis of graphene on copper surfaces has been of particular interest due to its simplicity and cost effectiveness6–15. However, the rates of growth for graphene by CVD on copper are less than 0.4 μm s–1, and therefore the synthesis of large, single-crystal graphene domains takes at least a few hours. Here, we show that single-crystal graphene can be grown on copper foils with a growth rate of 60 μm s–1. Our high growth rate is achieved by placing the copper foil above an oxide substrate with a gap of ~15 μm between them. The oxide substrate provides a continuous supply of oxygen to the surface of the copper catalyst during the CVD growth, which significantly lowers the energy barrier to the decomposition of the carbon feedstock and increases the growth rate. With this approach, we are able to grow single-crystal graphene domains with a lateral size of 0.3 mm in just 5 s. 

Ultrafast Growth of Single-crystal Graphene Assisted by a Continuous Oxygen Supply.pdf

Copyright(c)版权所有 永利集团纳米化学研究中心 北京市海淀区成府路202号 77779193永利集团A区4层 100871 010-62757157
最后更新日期:201828 网站统计: